[PDF] SIQUAL 3505 Steel

Datasheet for Steel Grades Tool Steel 100Cr6

Bearing-Steel-100Cr6-AUSA

100Cr6 HEAT TREATMENTS - APPROXIMATE TEMPERATURES Annealed ºC Tempered ºC 720-800 830 - 870 150-300 Oil Quenched ºC Steel with great wear resistance It has little deformation in the quenching A minimum of 2,5 mm in radius is recommended to machine in order to eliminate the decarburized area

Catamold 100Cr6 - WERKTUIGBOUWNL

BASF Aktiengesellschaft Catamold® 100Cr6 Product Description Ready-to-mold granules for the production of sintered components in a low-alloy bearing steel type 100Cr6 using the BASF system Standards DIN 1 3505, 100Cr6 AISI E52100; UNS G52986 Typical composition after Sintering C Cr Fe 0 80 – 1 05 1 35 – 1 65 Balance

Quality 100Cr6 (EN ISO 683-17) - MT Acciai

Quality 100Cr6 (EN ISO 683-17) PROPERTIES AND EMPLOYEMENTS Is it the most used steel for what concerns the fabrication of bearings and roller balls For the con-struction of roller balls, this steel has a good hardenability, diameters up to 30 mm, good inalterabili-

STUDY OF THE MACHINABILITY OF HARDENED 100CR6 BEARING STEEL

In the present investigation, the workpiece material is an 100Cr6 steel bars This material is being used for the manufacturing of the bearing rings and automotive components The nominal chemical composition of 100Cr6 steel is shown in Table 1 These bars are nominally of 54 mm diameter and were cut to 400 mm length prior to heat treatment

CHROME STEEL AISI 52100 100Cr6 - ROLLING COMPONENTS

Low alloy martensitic chrome steel, AISI 52100 thanks to its high hardness, wear resistance, surface finishing and dimensional precision, it is widely used to manufacture mechanical

SIQUAL 3505 Steel

SIQUAL 3505 OCR4ES 1 3505 100Cr6 100Cr6 5210 Chemical Composition (in weight ) C Si Mn Cr Mo Ni V W Others 0 97 0 25 0 35 1 50 - max 0 30 - - max 0 30 Cu Description 52100 is a high carbon, chromium containing low alloy steel that is through hardening and noted in particular for use as bearings Applications

Materials for Rolling Bearing Technology

100Cr6 (reference 2) Martensitic hardening, thermal stabilisation S0 Characteristics, special features Base material Through hardening rolling bearing steel 100Cr6 (SAE52100/SUJ2/STB2/ GCr15), modified where necessary Depending on the wall thickness of the components, it may be necessary to use a higher grade alloy taking account of hardenability

Durapur 3505 - dew-stahlcom

100Cr6 130 Durapur 3505 ist ein klassischer Wälzlagerstahl Diese Güte eignet sich zur Herstellung von Kugellagern, Rol-lenlagern und Nadellagern Durapur 3505 wird weiterhin im Maschinenbau für verschleißbeanspruchte Bauteile, z B für Pumpenwellen in verschleißfördernden Medien und für Bauteile in Automobileinspritzanlagen verwen-